Colorful Epoxy Resin Boat Marine Ballast Tank Anticorrosive Coating Paint
A Video of Marine Paint Project Construction.
TKEH-705 Modified Epoxy Ballast Tank Anticorrosive Coating (Gray)
As anticorrosive coatings for ballast tanks, waste water tanks and sewage pipes, etc.
0~10% by weight
May be applied by spray, brush, or roller.
FXH-4 Epoxy Thinner
base/curing agent=8/1 by weight
Dry Film Thickness:100μm/coat Wet Film Thickness:185μm/coat
Theoretical: 0.21kg/m2/100μm 0.148L/m2/100μm
Practical:Depending on the surface treatment, environment and application methods.
Dry to touch
Dry to handle
2K packaging: A kit 22.5kg contains Part A 20kg and Part B2.5kg.
1.Remove salts and other water soluble contaminants with fresh water.
2.Remove oil in accordance with the solvent cleaning standard SSPC-SP1.
3.Remove rust and scale by sand blasting to ISO Sa 2.5 (SSPC-SP10)
4.Remove the contaminants like dust with high pressure blower.
5.Confirm the surface clean and dry before working.
Substrate: Bare steel
Top Coat: Refer to our coating system
The following shall be guaranteed during any paint applications:
Packaging & Transportation
RPEH-405 High-Build Modified Epoxy Anticorrosive Primer
♦ High-build anticorrosive paint
♦ Excellent resistance to sea water penetration corrosion
♦ Firm film with wear-resistant
♦ Excellent adhesion
♦ Excellent compatibility
As maintenance antirust primer for newly-built ships or old ships.
Theoretical Coverage Rate
Temperature: 10°C 20°C 30°C
Dry to touch: 2hrs 1.5hrs 1hrs
Dry to handle: 14hrs 10hrs 8hrs
Main agent : firming agent = 8:1 by weight
2 component package, total 22.5 kg: part A 20kg, part B 2.5 kg