ACEH-202 Modified Epoxy Antiabrasive Innoxious Hold Marine Paint

FOB Reference Price:Get Latest Price
US $3.1-7 / Kilograms | 100 Kilogram/Kilograms (Min. Order)
Report Suspicious Activity
Overview
Quick Details
CAS No.:
FX
Other Names:
Marine Paint
MF:
FX
EINECS No.:
FX
Place of Origin:
Tianjin, China (Mainland)
Main Raw Material:
Epoxy
Usage:
Appliance Paint, Boat Paint
Application Method:
Roller
State:
Liquid Coating
Brand Name:
FUXI
Model Number:
ACEH-202
Color:
Aluminum gray
Type:
Marine paint
Mixing Ratio:
Two components:base/curing agent=8/1 by weight
Solid Content:
78%
Specific Gravity:
1.42
Shelf Life:
1year
Film Thickness:
Dry film thickness 100μm/coat
Thinner:
FXH-4 Epoxy Thinner
Packing:
2K packaging: A kit 22kg contains Part A 20kg and Part B2kg.
Brand:
FUXI
SupplyAbility
SupplyAbility:
12000 Ton/Tons per Year
Packaging & Delivery
Packaging Details
2K packaging: A kit 22kg contains Part A 20kg and Part B2kg.
Port
Xingang, Tianjin
Lead Time :
Shipped in 7 days after payment

ACEH-202 Modified Epoxy Antiabrasive Innoxious Hold Marine Paint

 

Product Description
1.Product Basic Info:
ACEH-202 Modified Epoxy Ship Bottom Anticorrosive Primer(Aluminum)
UsesAs antirust primer for the part of under waterline of the newly-built ships or old ships.
ColorAluminum gray
Shelf life12 months
Packing2K packaging: A kit 22kg contains Part A 20kg and Part B2kg.
Coating systemSteel: Bare steel
Top coat: refer to our coating system
2.Picture Display:

3.Characteristics:

¶ Excellent resistance to sea water and penetration corrosion.

¶ Tough film with wear resistance and excellent adhesion.

¶ High-build workability.

¶ Good adhesion force.

Application conditions

Airless spray

Recommended

Nozzle orifice

0.4~0.5mm

Nozzle pressure

100~150kg/cm²

Thinning ratio

0~10% .by weight

May be applied by spray, brush, or roller.

Thinner

FXH-4 Epoxy Thinner

Mixing ratio

Two components

base/curing agent=8/1 by weight

Pot life

Temperature

10°C

20°C

30°C

Pot life

10hrs

8hrs

6hrs

Film thickness

Dry film thickness 100μm/coat

Solid content

78%

Specific gravity

1.42

Coverage rate

Theoretical

0.21kg/m2/100μm 0.142L/m2/100μm

Actual:Depending on the surface treatment, environment and application methods.

Dry time

Temperature

10°C

20°C

30°C

Dry to touch

2hrs

1.5hrs

1hrs

Dry to handle

14hrs

10hrs

8hrs

Coating interval

Min.

14hrs

10hrs

8hrs

Max.

4.Application Show:

A Video of Marine Paint Project Construction.

5.Surface preparation:

1.Remove salts and other water soluble contaminants with fresh water.

2.Remove oil in accordance with the solvent cleaning standard SSPC-SP1.

3.Remove rust and scale by sand blasting to ISO Sa 2.5 (SSPC-SP10)

4.Remove the contaminants like dust with high pressure blower.

5.Confirm the surface clean and dry before working.

Popular Types

RPEH-405 High-Build Modified Epoxy Anticorrosive Primer

(Iron Red)

 

♦ High-build anticorrosive paint

♦ Excellent resistance to sea water penetration corrosion 

♦ Firm film with wear-resistant

♦ Excellent adhesion

♦ Excellent compatibility

 

Usage:

As maintenance antirust primer for newly-built ships or old ships.

 

Suitable Substrate:

Bare steel

 

Color:

Iron Red

Film Thickness

100μm/layer

Theoretical Coverage Rate

0.21kg/m2/50μm

Drying Time

Temperature:      10°C      20°C     30°C

Dry to touch:        2hrs      1.5hrs     1hrs

Dry to handle:     14hrs     10hrs      8hrs   

Mixing Ratio

Main agent : firming agent = 8:1 by weight

Package

2 component package, total 22.5 kg: part A 20kg, part B 2.5 kg