TKEH-706 Antifouling Polyurethane Water Based Marine Cargo Tank Paint

FOB Reference Price:Get Latest Price
US $3.1-7 / Kilograms | 100 Kilogram/Kilograms (Min. Order)
Report Suspicious Activity
Overview
Quick Details
CAS No.:
FX
Other Names:
Marine Paint
MF:
FX
EINECS No.:
FX
Place of Origin:
Tianjin, China (Mainland)
Main Raw Material:
Epoxy
Usage:
Appliance Paint, Boat Paint
Application Method:
Roller
State:
Liquid Coating
Brand Name:
FUXI
Model Number:
TKEH-706
Color:
White, Gray
Type:
Marine paint
Mixing Ratio:
Two components: base/curing agent=8/1 by weight
Solid Content:
78%
Specific Gravity:
1.45
Shelf Life:
1year
Dry Film Thickness:
100μm/coat
Wet Film Thickness:
185μm/coat
Thinner:
FXH-4 Epoxy Thinner
Packing:
2K packaging: A kit 24.5kg contains Part A 21kg and Part B3.5kg.
SupplyAbility
SupplyAbility:
12000 Ton/Tons per Year
Packaging & Delivery
Packaging Details
2K packaging: A kit 24.5kg contains Part A 21kg and Part B3.5kg.
Port
Xingang, Tianjin
Lead Time :
Shipped in 7 days after payment

TKEH-706 Antifouling Polyurethane Water Based Marine Cargo Tank Paint

 

Product Description
1.Product Basic Info:

Item

TKEH-706Modified Epoxy Abrasion Resistant Nontoxic Cargo Tank Coating

Uses

As anticorrosive coatings for the abrasive blasted steel and the holds of bulk cargo ships.

Color

White, Gray

Thinner

FXH-4 Epoxy Thinner

Shelf Life

12months

Package

2K packaging: A kit 24.5kg contains Part A 21kg and Part B3.5kg.

Safety Precautions

The following shall be guaranteed during any paint applications:

  • Avoid skin and eye contact.
  • In case of skin or eye contact, flush with large amount of water and immediately get medical attention.
  • Assure well-ventilated working place.
  • Take precautions of the risks of fire or explosion.
  • Observe all health and safety regulations on site.
 
2.Picture Display:
3.Other Info:

Application Conditions

Airless Spray

Recommended

Nozzle Tip

0.4~0.5mm

Nozzle Pressure

100~150kg/cm2

Thinning Ratio

0~10% by Weight

May be applied by spray, brush, or roller.

Mixing Ratio

Two component

base/curing agent=8/1 by weight

Pot Life

Temperature

10°C

20°C

30°C

Pot life

10hrs

8hrs

6hrs

Film thickness

Dry film thickness :100μm/coat    

Wet film thickness :185μm/coat

Solid content

78%

Specific gravity

1.45

Spreading Rate

Theoretical

0.22kg/m2/100μm 0.148L/m2/100μm

Practical

varies depending on the surface treatment, environment, application method

Drying time

 

Temperature

10°C

20°C

30°C

Dry To Touch

2hrs

1.5hrs

1hrs

Dry To Handle

14hrs

10hrs

8hrs

Coating interval

Min.

14hrs

10hrs

8hrs

Max.

4.Appliaction:

Surface Preparation

Remove salts and other water soluble contaminants with fresh water.

Remove oil in accordance with the solvent cleaning standard SSPC-SP1. 

Remove rust and scale by sand blasting to ISO Sa 2.5 (SSPC-SP10).

Remove the contaminants like dust with high pressure blower.

Confirm the surface clean and dry before working.


Coating System

Substrate: bare steel

Top coat: reference to our coating system.

 

5.Packaging & Transportation

Popular Types

RPEH-405 High-Build Modified Epoxy Anticorrosive Primer

(Iron Red)

 

♦ High-build anticorrosive paint

♦ Excellent resistance to sea water penetration corrosion 

♦ Firm film with wear-resistant

♦ Excellent adhesion

♦ Excellent compatibility

 

Usage:

As maintenance antirust primer for newly-built ships or old ships.

 

Suitable Substrate:

Bare steel

 

Color:

Iron Red

Film Thickness

100μm/layer

Theoretical Coverage Rate

0.21kg/m2/50μm

Drying Time

Temperature:                10°C                20°C                30°C

Dry To Touch:                 2hrs              1.5hrs               1hrs

Dry To Handle:             14hrs               10hrs               8hrs 

Mixing Ratio

Main agent : firming agent = 8:1 by weight

Package

2 component package, total 22.5 kg: part A 20kg, part B 2.5 kg

Our Test Show